Material Properties
| Ultraliner PVC Alloy Material Properties |
|
Higher-Compliance [complying with ASTM F 1871] Ultraliner PVC Alloy Pipeliner |
Higher-Stiffness [complying with ASTM F 1504] Ultraliner PVC Alloy Pipeliner |
|
| size availability: | Available in any size from 4" to 30" | Available in any size from 4" to 15" |
| industry standards: |
ASTM D 1784 material standard ASTM F 1871 product standard ASTM F 1867 installation standard |
ASTM D 1784 material standard ASTM F 1504 product standard ASTM F 1947 installation standard |
| Material Properties: | ||
| base resin: | poly(vinyl chloride) homopolymer | poly(vinyl chloride) homopolymer |
|
izod impact resistance: [ASTM D 256] |
15 ft-lb/in | 15 ft-lb/in |
|
tensile modulus: [ASTM D 638] |
155,000 psi (1069 MPa) | 280,000 psi (1930 Mpa) |
|
tensile strength [ASTM D 638]: |
3,600 psi (25 MPa) | 5,000 psi |
|
flexural modulus: [ASTM D 790] |
145,000 psi (1000 MPa) | 280,000 psi (1930 Mpa) |
| recommended long-term modulus reduction: | 25% reduction, 75% retention | 65% reduction, 35% retention |
|
flexural strength: [ASTM D 790] |
4,100 psi (28 MPa) | 5,000 psi |
|
heat deflection temperature: [ASTM D 648] |
115 degrees F (46 C) | 140 degrees F |
| chemical resistance: | suitable for use under general sanitary sewer conditions | suitable for use under general sanitary sewer conditions |
For information to assist you in determining which product is appropriate for your specific project needs we invite you to compare the advantages of each of our products.
Click here for Ultraliner Chemical Resistance Chart